Study On Thermal Fatigue Behaviour Of Plasma Sprayed Yttria-Zirconia Thermal Barrier Coatings (TBCS) Systems On Aluminium Alloy | |||||||||
Author Name |
Dipak Kumar, K.N.Pandey | |||||||||
Affilition |
Mechanical Engineering Department MNNIT Allahabad | |||||||||
Pages |
19-22 | |||||||||
Abstract |
Abstract: Yttria stabilized zirconia (YSZ) thermal barrier coatings (TBCs) systems were fabricated by plasma spray process on 2024 aluminium alloys (AA). Thermal fatigue behaviour of as sprayed TBCs systems at 6000 C was studied. The results indicated that cracking was only responsible for thermal fatigue failure mode. The failures of YSZ TBCs systems on 2024AA were observed due to the multiple cracks mode only. The results shows four types of cracks were formed in TBCs systems on 2024 AA, i.e., vertical cracks, horizontal crack, propagating crack, and penetrating crack. | |||||||||