Antibacterial Properties of Stainless Steel Coated on Ti6Al4V Alloy | |||||||||
Author Name |
Ridvan Yamanoglu, Fuad Khoshnaw, Fetiye Kolayli, Huseyin Uzuner | |||||||||
Affilition |
Metallurgical and Materials, Engineering Department, Kocaeli University, Turkey School of Engineering and Sustainable Development, De Montfort University, Leicester, United Kingdom Department of Microbiology, Kocaeli University, Kocaeli, Turkey | |||||||||
Pages |
53-56 | |||||||||
Abstract |
Titanium alloys and stainless steel type 316Lare used in biomedical applications due to their high corrosion resistance and good biocompatibility properties. In this study, a functionally graded material composed of titanium and stainless steel was fabricated using a powder metallurgical technique. Ti6Al4V alloy powder was placed as a substrate into a graphite crucible and stainless steel powder was added as a thin layer on the Ti6Al4V powder. The two layers were consolidated in-situ using a uniaxial hot press. The sintering process was carried out at 1050 ÂșC for 30 minutes under 50 MPa. The pressure was maintained during the whole sintering process. A disc shape compact of 20 mm diameter and 5 mm thickness was obtained after sintering. The samples were metallographically prepared and their antibacterial properties were evaluated. A strong bonding was observed between the Ti6Al4V substrate and the 316L stainless steel layer, and no bacteria were observed on the stainless steel surface. Keywords - Antibacterial activity, Stainless steel 316L, Ti6Al4V, pressure assisted sintering technique. | |||||||||