Paper Title |
Effect of High Power Ultrasonic Irradiation to the Magnetic Properties of Bafe12o19/Cofe2o4 Composite | |||||||||
Author Name |
Gemi Nastiti, Azwar Manaf | |||||||||
Affilition |
Postgraduate Program of Materials Science Study, Department of Physics, Faculty of Mathematics and Natural Sciences, UniversitasIndonesia.Kampus UI, Jl. Salemba Raya No. 04 Jakarta 10430, Indonesia. | |||||||||
Pages |
132-135 | |||||||||
Abstract |
Magnetic properties of composite magnets made of Barium Hexaferrite (BHF) and CoFe 2 O 4 were reported in this paper. Effect of variation ultrasonic irradiation caused to the magnetic properties of the composite. The two types of magnetic particles have a high total magnetization value which was required for permanent magnet applications. Both CoFe 2 O 4 and BHF were synthesized through mechanical alloying coupled with high frequency ultrasonic irradiation. In this respect, mechanically milled BHF precursors was sintered at a temperature of 1250 0 C for 2 hours leading to single phase powders. A similar method was also employed in the preparation of CoFe 2 O 4 materials, but this required a relatively longer sintering time up to 12 hours at a sintering temperature of 900 0 C. Composite magnets were obtained after sintering the mechanically mixed the two types as constituted components of the composite. The enhancement in remanent magnetization raised aboutthe effect of grain exchange interaction between hard and soft magnetic phases.The results studied by XRD, Permagraph and SEMrespectively. Index terms- BaFe 12 O 19 , CoFe 2 O 4 , Composite, Permanent magnet. | |||||||||